Temperature dependence of the electrical resistivity and the anisotropic magnetoresistance (AMR) of electrodeposited Ni-Co alloys
Létrehozó:
Tóth, Bence
Péter, László
Révész, Ádám
Pádár, József
Bakonyi, Imre
Kiadó:
Springer-Verlag
Dátum:
2010
Téma:
QC04 Electricity. Magnetism. Electromagnetism / villamosság, mágnesesség, elektromágnessesség
QC06 Physics of condensed matter / szilárdtestfizika
Tartalmi leírás:
The electrical resistivity and the anisotropic magnetoresistance (AMR) was investigated for Ni Co alloys at and below room temperature. The Ni Co alloy layers having a thickness of about 2 micron were prepared by electrodeposition on Si wafers with evaporated Cr and Cu underlayers. The alloy composition was varied in the whole concentration range by varying the ratio of Ni sulfate and Co sulfate in the electrolyte. The Ni Co alloy deposits were investigated first in the as deposited state on the substrates and then, by mechanically stripping them from the substrates, as self supporting layers both without and after annealing. According to an X ray diffraction study, a strongly textured face centered cubic (fcc) structure was formed in the as deposited state with an average grain size of about 10 nm. Upon annealing, the crystal structure was retained whereas the grain size increased by a factor of 3 to 5, depending on alloy composition. The zero field resistivity decreased strongly by annealing due to the increased grain size. The annealing hardly changed the AMR below 50 at.% Co but strongly decreased it above this concentration. The composition dependence of the resistivity and the AMR of the annealed Ni Co alloy deposits was in good quantitative agreement with the available literature data both at 13 K and at room temperature. Both transport parameters were found to exhibit a pronounced maximum in the composition range between 20 and 30 at.% Co and the data of the Ni Co alloys fitted well to the limiting values of the pure component metals (fcc Ni and fcc Co). The only theoretical calculation reported formerly on fcc Ni Co alloys yielded at T = 0 K a resistivity value smaller by a factor of 5 and an AMR value larger by a factor of about 2 than the corresponding low temperature experimental data, although the theoretical study properly reproduced the composition dependence of both quantities.
Típus:
Article
PeerReviewed
Formátum:
application/pdf
Azonosító:
Tóth, Bence and Péter, László and Révész, Ádám and Pádár, József and Bakonyi, Imre (2010) Temperature dependence of the electrical resistivity and the anisotropic magnetoresistance (AMR) of electrodeposited Ni-Co alloys. European Physical Journal B, 75 (2). pp. 167-177. ISSN 1434-6028 (nyomtatott), 1434-6036 (online)